H42 vs H19
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
H42
Tool Steel
H42 is chemically a molybdenum high-speed steel (close to the M2 family) that ASTM classes with the hot work steels because of its high working hardness and hot strength. It is used for hot punches and extrusion tools needing near-HSS edge retention.
Standards: AISI H42
H19
Tool Steel
H19 is a tungsten-cobalt hot work steel with red hardness well beyond the 5% chromium family. It serves the hottest die positions — brass extrusion and severe hot heading — where H13 softens too fast.
Standards: AISI H19
Chemical composition compared (%)
| Element | H42 | H19 |
|---|---|---|
| C | 0.55–0.70 | 0.35–0.45 |
| Si | ≤0.45 | 0.20–0.50 |
| Mn | ≤0.40 | 0.20–0.50 |
| Cr | 3.75–4.50 | 4.00–4.75 |
| Mo | 4.50–5.50 | — |
| W | 5.75–6.75 | 3.75–4.75 |
| V | 1.75–2.25 | 1.65–2.25 |
| Co | — | 4.00–4.75 |
Properties compared
| Property | H42 | H19 |
|---|---|---|
| Delivery condition | Annealed | Annealed |
| Working hardness | 48–58 HRC | 40–52 HRC |
| Density | 8.10 g/cm³ | 8.00 g/cm³ |
| Class note | Molybdenum high-speed composition classed as hot work | — |
| Hot hardness | — | Very high (cobalt-bearing) |