1.2067
Data under review1.2067 is a through-hardening chromium cold work steel of the bearing-steel family (similar to 100Cr6/L3 practice). It gives high hardness and wear resistance in small tools and precision parts at low alloy cost.
Chemical composition
| Element | Content (%) |
|---|---|
| C | 0.95–1.10 |
| Si | 0.15–0.35 |
| Mn | 0.20–0.40 |
| Cr | 1.35–1.65 |
Weight percent, per the governing standard ranges. Actual values per heat are on the mill certificate.
Properties
| Delivery condition | Annealed |
| Hardness (hardened) | 58–64 HRC |
| Density | 7.85 g/cm³ |
Heat treatment
Harden 830–860 °C oil; temper 150–250 °C.
Equivalent grades
| Standard | Designation |
|---|---|
| din | 1.2067 |
| aisi | L3 (near) |
| jis | SUJ2 (near) |
| gb | Cr2 (near) |
Compare side by side: 1.2067 vs O1 · 1.2067 vs L2
Equivalents overlap in chemistry and use but are not always identical — see our equivalents guide before substituting in certified designs.
Applications & Processing
Applications: Small punches and dies, gauges, bushings, ball and roller parts, measuring tools.
Processing: Oil hardening with moderate distortion; cleaner (bearing-grade) melts are used where fatigue or polish matters.