20CrMnTi vs 4820
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
20CrMnTi
Alloy & Engineering Steel
20CrMnTi is China’s dominant carburizing gear steel (GB/T 3077): a Cr-Mn steel micro-alloyed with titanium for grain control, produced in huge tonnage for automotive and industrial gearboxes.
Standards: AISI 4820 (near) · GB 20CrMnTi (GB/T 3077)
4820
Alloy & Engineering Steel
4820 is the higher-carbon companion of 4815 in the 3.5% nickel carburizing family, giving a stronger core at the same case performance. It is used for large, heavily loaded gears in mining and aerospace service.
Standards: AISI 4820
Chemical composition compared (%)
| Element | 20CrMnTi | 4820 |
|---|---|---|
| C | 0.17–0.23 | 0.18–0.23 |
| Si | 0.17–0.37 | 0.15–0.35 |
| Mn | 0.80–1.10 | 0.50–0.70 |
| P | ≤0.035 | ≤0.035 |
| S | ≤0.035 | ≤0.040 |
| Cr | 1.00–1.30 | — |
| Ti | 0.04–0.10 | — |
| Ni | — | 3.25–3.75 |
| Mo | — | 0.20–0.30 |
Properties compared
| Property | 20CrMnTi | 4820 |
|---|---|---|
| Tensile strength | ≥1080 MPa (GB/T 3077 reference, carburized + Q&T blank) | — |
| Yield strength | ≥850 MPa (reference) | — |
| Case hardness (carburized) | 58–64 HRC | 58–63 HRC |
| Density | 7.85 g/cm³ | 7.85 g/cm³ |
| Core tensile strength | — | 850–1100 MPa (typ.) |
Sourcing either grade?
Nasteel stocks both families from Shenzhen with EN 10204 3.1 mill certificates by heat number.
Ask for a quotationSee full data sheets: 20CrMnTi · 4820. Substitution decisions for certified parts stay with the design authority.