1022 vs 1524
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
1022
Carbon Steel
1022 is a low carbon, higher manganese steel with better hardenability than 1020 at the same carbon level. It is used for carburized parts and moderately loaded components where 1020 would be too soft in the core.
Standards: DIN C22 (near) · AISI 1022 · JIS S20C (near) · GB 20Mn (near)
1524
Carbon Steel
1524 is a low carbon steel with 1.35–1.65% manganese, giving noticeably better hardenability and core strength than 1020/1022. It is a cost-effective carburizing steel for larger case-hardened parts.
Standards: AISI 1524 · GB 20Mn (near)
Chemical composition compared (%)
| Element | 1022 | 1524 |
|---|---|---|
| C | 0.18–0.23 | 0.19–0.25 |
| Mn | 0.70–1.00 | 1.35–1.65 |
| P | ≤0.040 | ≤0.040 |
| S | ≤0.050 | ≤0.050 |
Properties compared
| Property | 1022 | 1524 |
|---|---|---|
| Tensile strength | 400–480 MPa (hot rolled, typ.) | 440–540 MPa (hot rolled, typ.) |
| Density | 7.85 g/cm³ | 7.85 g/cm³ |
| Weldability | Good | — |
Sourcing either grade?
Nasteel stocks both families from Shenzhen with EN 10204 3.1 mill certificates by heat number.
Ask for a quotationSee full data sheets: 1022 · 1524. Substitution decisions for certified parts stay with the design authority.