1084 vs 1080
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
1084
Carbon Steel
1084 is a eutectoid-plus high carbon steel popular for blades and springs because its simple chemistry heat treats forgivingly in small workshops. The manganese level gives slightly deeper hardening than 1095.
Standards: DIN C85 type (near) · AISI 1084 · JIS SK5 family (near) · GB 85 (near)
1080
Carbon Steel
1080 sits at the eutectoid carbon level: fully pearlitic when normalized and capable of high hardness after quenching. It is a classic spring and blade steel for thicker sections than 1075 handles.
Standards: DIN C80 type (near) · AISI 1080 · JIS SK5 family (near) · GB 80
Chemical composition compared (%)
| Element | 1084 | 1080 |
|---|---|---|
| C | 0.80–0.93 | 0.75–0.88 |
| Mn | 0.60–0.90 | 0.60–0.90 |
| P | ≤0.040 | ≤0.040 |
| S | ≤0.050 | ≤0.050 |
Properties compared
| Property | 1084 | 1080 |
|---|---|---|
| Tensile strength | 820–980 MPa (normalized, typ.) | 800–950 MPa (normalized, typ.) |
| Hardness (hardened) | 58–63 HRC (thin sections) | — |
| Density | 7.85 g/cm³ | 7.85 g/cm³ |
| Hardness (spring temper) | — | 45–52 HRC typical |