347H vs 347
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
347H
Stainless Steel
347H is the high-carbon niobium-stabilised grade for creep-range pressure service, combining the sensitisation resistance of 347 with code creep-rupture values. It is widely used in refinery and steam plant.
Standards: DIN 1.4912 · AISI 347H · JIS SUS347 · GB 07Cr19Ni11Nb
347
Stainless Steel
347 is the niobium-stabilised counterpart of 321, preferred for welded high-temperature service because niobium carbides are more stable during welding thermal cycles. It is a standard grade for aircraft exhausts and refinery equipment.
Standards: DIN 1.4550 · AISI 347 · JIS SUS347 · GB 06Cr18Ni11Nb
Chemical composition compared (%)
| Element | 347H | 347 |
|---|---|---|
| C | 0.04–0.10 | ≤0.08 |
| Si | ≤0.75 | ≤0.75 |
| Mn | ≤2.00 | ≤2.00 |
| P | ≤0.045 | ≤0.045 |
| S | ≤0.030 | ≤0.030 |
| Cr | 17.00–19.00 | 17.00–19.00 |
| Ni | 9.00–13.00 | 9.00–13.00 |
| Nb | 8×C–1.00 | 10×C–1.00 |
Properties compared
| Property | 347H | 347 |
|---|---|---|
| Delivery condition | Annealed | Annealed |
| Hardness | ≤217 HB (annealed) | ≤217 HB (annealed) |
| Tensile strength | 515–690 MPa | 515–690 MPa |
| Density | 7.90 g/cm³ | 7.90 g/cm³ |
| Creep service | Rated for pressure service above ~525 °C | — |
Sourcing either grade?
Nasteel stocks both families from Shenzhen with EN 10204 3.1 mill certificates by heat number.
Ask for a quotationSee full data sheets: 347H · 347. Substitution decisions for certified parts stay with the design authority.